Silicone Rubber
Self-adhesive Liquid Silicone Rubber
ME8100- XXA/B
· Description: This grade is mainly designed for pure PC or glass fiber-reinforced PC substrates with outstanding self-adhesive properties. The substrate does not need to be primed before use, and the silicone rubber maintains good adhesion with the substrate after molding.
· Features: Self-adhesive, high performance.
· Applications: Suitable for producing colored 3Celectronic products, kitchenware, medical instruments, and other encapsulated products with PC substrates.
·Testing:A/B mixingratio of 1:1,130 ℃×10min×17MPa.
| Model | Unit | ME8100-XXA/B | |||||
| 20 | 30 | 40 | 50 | 60 | 70 | ||
| Appearance | / |
Translucent/milky white |
|||||
| Viscosity | Pa's | 1000 | 2000 | 3000 | 5000 | 5000 | 6000 |
|
Hardness |
ShoreA |
20 | 30 | 40 | 50 | 60 | 70 |
| Density | g/cm³ | 1.10 | 1.11 | 1.12 | 1.13 | 1.13 | 1.13 |
| Tensile strength | MPa | 6 | 7 | 8 | 8 | 8 | 7 |
| Elongation | % | 700 | 600 | 500 | 450 | 400 | 300 |
| Tear strength | kN/m | 15 | 20 | 30 | 30 | 30 | 30 |
ME8300-XXA/B
·Description: This grade is mainly designed for pure PC or glass fiber-reinforced PC substrates with outstanding self-adhesive properties. The substrate does not need to be primed before use, and the silicone rubber maintains good adhesion with the substrate after molding.
· Features: Self-adhesive, high performance.
·Applications: Suitable for producing colored 3C electronic products, kitchenware, medical instruments, and other encapsulated products with PC substrates.
·Testing:A/B mixingratio of 1:1,130 ℃×10min×17MPa.
| Model | Unit | ME8300-XXA/B | |||||
| 20 | 30 | 40 | 50 | 60 | 70 | ||
| Appearance | / |
Translucent/milky white |
|||||
| Viscosity | Pa's | 1000 | 2000 | 2000 | 2000 | 3000 | 5000 |
|
Hardness |
ShoreA |
20 | 30 | 40 | 50 | 60 | 70 |
| Density | g/cm³ | 1.10 | 1.11 | 1.13 | 1.13 | 1.13 | 1.13 |
| Tensile strength | MPa | 6 | 7 | 8 | 8 | 8 | 7 |
| Elongation | % | 700 | 600 | 500 | 450 | 400 | 300 |
| Tear strength | kN/m | 15 | 20 | 30 | 30 | 30 | 30 |